Woven Flexible Tarpaulin

Woven Flexible Tarpaulin

Fire retardant, waterproof, rotproof and UV-resistant
Band reinforced tarpaulin in sheet of 4×6 m developed by international research project and designed for long outdoor use in all climates
Woven high density polyethylene (HDPE) black fibres fabric coated on both sides with low density polyethylene (LDPE) coating
Highly recommended for family shelter protection

Water proof

UV Stabilised

  • Fire retardant, waterproof, rotproof and UV-resistant
  • Band reinforced tarpaulin in sheet of 4x6 m developed by international research project and designed for long outdoor use in all climates
  • Woven high density polyethylene (HDPE) black fibres fabric coated on both sides with low density polyethylene (LDPE) coating
  • Highly recommended for family shelter protection
Size/Sheet 4 x 6 m ±1%
Size / roll 4 x 60 m ±1%
Specific sheet without bands weight 90 ±20 g under ISO 3801 (equivalent to min 170 to 210 gsm max)
Complete sheet with bands weight Plain sheet specific weight plus 10% additional weight for reinforcement bands under ISO 3801
Total weight From min 187 to 231 gsm. Specific weight of bands from min 150 to 200 gsm max
Sheet / roll Woven HDPE black fibers fabric, double-side LDPE coating, reinforced with 6 bands of 75 ±3% mm width woven black HDPE fibers fabric and coated outside. Pre-punched 8 mm holes on the 2 side bands at 0.1 ±10% m intervals, positioned in the center of the bands (only the reinforcement bands are pre-punched, not the tarpaulin itself). Flame retardant EN13823+A1.
Tensile strength Min 500N, 15-35% elongation in warp and weft in plain sheet under ISO 1421-1.
UV resistance After 1500 hours UV under ASTM G53/94 (UVB 313 nm peak) minimum 80% of original value of the actual product and not less than 475N.
Reinforcement bands Min 700N as per ISO 1421-1, pulling lengthwise in a pre-punched 8 mm hole with a hook of 8 mm wire diameter, at 200 mm from the end of the band. UV resistance 80% of original value and not less than 665N.
Welding Only one is allowed, lengthwise. The tarpaulin tensile strength crossways at the place of welding under ISO 1421-1 minimum 50% of original value and not less than 400N.